項 目 \ 牌 號 |
硅磚 |
粘土質 Fire clay |
特種高鋁質Special High Alumina |
Cordierite堇青石質 |
|||||||
|
|
|
JNLA |
JN40a |
JN40b |
BGZ-65 |
BGZ-70 |
JLZ-75 |
JHL-75 |
SDHA60S |
|
|
|
Al2O3 % |
≤1.5 |
30～36 |
≥40 |
≥40 |
|
|
≥75 |
≥75 |
≥60 |
≥40 |
|
|
Fe2O3 % |
≤1.5 |
≤2.5 |
≤2.0 |
≤2.0 |
|
|
|
≤0.8 |
≤1.5 |
|
|
|
SiO2 % |
≥94.5 |
|
|
|
≥65 |
≥70 |
|
|
|
|
|
|
K2O+Na2O % |
CaO≤2.5 |
|
|
|
|
|
|
≤0.5 |
|
MgO≥3 |
|
|
耐火度 ℃ |
|
≥1690 |
≥1730 |
≥1730 |
|
|
≥1790 |
≥1790 |
≥1790 |
≥1580 |
|
|
荷重軟化溫度 ℃ |
KD≥1650 |
|
Ta≥1450 |
Ta≥1400 |
Ta≥1320 |
Ta≥1350 |
KD≥1550 |
KD≥1650 |
Ta≥1640 |
|
|
|
重燒線變化率 % |
1450℃×2h |
|
|
|
|
|
1500℃×2h |
1500℃×2h |
|
1300℃×2h |
|
|
顯氣孔率 % |
≤22 |
≤24 |
≤24(22) |
≤20 |
≤24 |
≤22(24) |
≤21(23) |
≤20 |
≤18 |
≤20 |
≤30 |
|
體積密度 g/cm3 |
真密度 |
真密度 |
≥2.0 |
≥2.0 |
≥2.0 |
|
|
|
≥2.65 |
≥2.4 |
|
|
常溫耐壓強度 MPa |
≥40 |
≥35 |
≥25(20) |
≥35 |
≥30 |
≥35(25) |
≥40(30) |
≥65 |
≥90 |
≥50 |
≥15 |
|
熱震穩(wěn)定性,次(1100℃ 水冷) |
|
|
|
|
|
|
|
|
≥35 |
≥20 |
≥20 |
|
0.2MPa蠕變率 % |
殘余石英: ≤1.0% |
|
1050℃×25h |
1050℃×25h |
1500℃ |
1500℃× |
|
|
|||
|
熱膨脹率(參考) % |
≤1.28 |
≤1.30 |
|
≤0.6 |
≤0.6 |
|
|
|
|
≤0.6 |
|
|
用 途 |
爐底、爐壁 |
其它 |
蓄熱室大墻、格子磚 |
炭化室、燃燒室 |
爐門 |
||||||